FLEXOMER™ ETS-9066 NT 7
| Категория | VLDPE, Very Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | FLEXOMER™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
C4aaPm_FLEXOMER-ETS-9066-NT-7.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
FLEXOMER™ ETS -9066 NT 7 Very Low Density Polyethylene (VLDPE) Resin is intended for use in single or multi-layer blown-film constructions or thick sheets. Films extruded from ETS- 9066 NT 7 have a high tear strength, high impact strength, and high puncture resistance and are readily heat sealable. Addition of slip and antiblock agents should be considered for most applications.
- Excellent strength and toughness balance
- Flexible over wide temperature range
- Superior low temperature properties
- Broad sealing temperature range
- Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a (with restrictions)
- An additive present in this product limits use only in film form for food contact applications.
- Consult the regulations for complete details.
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.905 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Энергия прокола пленки | 4.52 | J | Internal method |
| Сила прокола пленки | 53.4 | N | Internal method |
| Сопротивление проколу пленки | 29.8 | J/cm³ | Internal method |
| Прочность пленки | |||
| MD | 47.2 | J/cm³ | ASTM D892 |
| TD | 59.6 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 130 | MPa | ASTM D882 |
| 2% secant, MD | 112 | MPa | ASTM D882 |
| 1% secant, TD | 129 | MPa | ASTM D882 |
| 2% secant, TD | 110 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 6.89 | MPa | ASTM D882 |
| TD : Yield | 6.21 | MPa | ASTM D882 |
| MD : Fracture | 34.1 | MPa | ASTM D882 |
| TD : Fracture | 25.8 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 330 | % | ASTM D882 |
| TD : Fracture | 560 | % | ASTM D882 |
| Ударное падение Dart | 870 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 270 | g | ASTM D1922 |
| TD | 440 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 87.8 | °C | ASTM D1525 |
| Температура плавления (DSC) | 99.0 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 48 | ASTM D2457 | |
| Haze | 11 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8mm) 熔体温度：416°F (213 °C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：59 rpm 冷冻线高度：30 分钟 (762 mm) |
| Тип материала | Категория | Производитель |
|---|---|---|
| FLEXOMER™ ETS-9078 NT 7 | VLDPE | The Dow Chemical Company |
| Clearflex® H&T CHH G0 | VLDPE | Versalis S.p.A. |
| FLEXOMER™ DFDA-1137 NT 7 | VLDPE | The Dow Chemical Company |
| Generic VLDPE | VLDPE | Generic |
| Jam PE 02X02 | VLDPE | Jam Petrochemical Company |
| Jam PE 01X01 | VLDPE | Jam Petrochemical Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved