NOVAPOL® LF-0219-A
| Категория | LDPE, Low Density Polyethylene |
| Производитель | NOVA Chemicals |
| Торговая марка | NOVAPOL® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
yFM0LY_NOVAPOL-LF-0219-A.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
NOVAPOL®LF-0219-A is a low density polyethylene material,. This product is available in North America and is processed by film extrusion.
NOVAPOL®The main features of the LF-0219-A are:
Typical application areas include:
NOVAPOL®The main features of the LF-0219-A are:
- Good processability
- Homopolymer
- accessible food
- Good sealing performance
- Good toughness
Typical application areas include:
- bag/lining
- packing
- Movie
- industrial applications
- food contact applications
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 38 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 170 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 190 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 18.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 250 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 550 | % | ASTM D882 |
| Ударное падение Dart 1(38 µm, Blown Film) | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 160 | g | ASTM D1922 |
| TD : 38 µm, blown film | 150 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 38.0 µm, Blown Film) | 37 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Low Friction Puncture 2(38.0 µm) | 180 | J/cm | Internal method |
| Film properties are typical of blown film extruded on a 1.5" extruder with 3" die and 35-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions. |
| Примечание | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Тип материала | Категория | Производитель |
|---|---|---|
| Riblene® FH 20 | LDPE | Versalis S.p.A. |
| Yanshan PE LD605 | LDPE | SINOPEC Beijing Yanshan Petrochemical |
| Daelim Po1y® LD-63 | LDPE | DAELIM INDUSTRIAL CO., LTD. |
| DINALEN® 30 | LDPE | DIOKI d.d. |
| PETILEN F2-21T | LDPE | PETKIM Petrokimya Holding A.S. |
| Petrothene® NA345009 | LDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved