DOWLEX™ NG 5085B
| Категория | LLDPE, Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOWLEX™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
w901Ne_DOWLEX-NG-5085B.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOWLEX™ NG 5085B is a Linear Low Density Polyethylene, 1-Octene copolymer, produced in the SOLUTIONTM technology. This resin presents better processability than conventional linear low density polyethylenes, with outstanding gloss and clarity maintaining the excellent mechanical properties and sealability of DOWLEX resins.
Main Characteristics:
Complies with:
Main Characteristics:
- Film for lamination
- Film for form, fill and seal
- Film of low thickness
- Film for coextrusion
- Film with high gloss and clarity
Complies with:
- U.S. FDA 21 CFR 177.1520 (c) 3.2a
- EU, No 10/2011
| Главная Информация | |
|---|---|
| Добавка |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сопротивление проколу пленки (50 µm) | 9.60 | J/cm³ | Internal method |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 50 µm | 8.10 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 10.3 | MPa | ASTM D882 |
| MD : Break, 50 µm | 25.8 | MPa | ASTM D882 |
| TD : Break, 50 µm | 24.5 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 50 µm | 720 | % | ASTM D882 |
| TD : Break, 50 µm | 730 | % | ASTM D882 |
| Ударное падение Dart (50 µm) | 470 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 1100 | g | ASTM D1922 |
| TD : 50 µm | 1200 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.0 µm) | 62 | ASTM D2457 | |
| Haze (50.0 µm) | 11 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| 吹塑薄膜的加工条件： 模具间隙：1.8 mm 温度：180°C - 200°C - 210°C 输出：116 kg/h 螺杆速度：82 rpm 挤出压力：298 巴 |
| Тип материала | Категория | Производитель |
|---|---|---|
| TOTAL Polyethylene Lumicene® M 2310 EP | LLDPE | TOTAL Refining & Chemicals |
| CERTENE™ LLBF-0822D | LLDPE | Muehlstein |
| Flexirene® MS 26 A | LLDPE | Versalis S.p.A. |
| Hanwha Total PE 8400F | LLDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Hanwha Total PE 8230F | LLDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| INEOS Wire & Cable BPD3801 | LLDPE | INEOS Olefins & Polymers Europe |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved