Описание материалов:
Clearflex FG 336 is a hexene copolymer linear low density polyethylene (C6-LLDPE), additivated with antioxidant, slip agent, antiblocking agent and processing aid, suitable for blown film extrusion.
Films obtained from Clearflex FG 336 show high rigidity together with optimum Elmendorf tear and impact resistance.
Main Application
Clearflex FG 336 is recommended for shipping sacks, where the perfect balance between additivation (in terms of slip and antiblocking) and mechanical performances leads to the manufacture of a tough and easy peelable film. Moreover, for its sealing characteristics, together with low temperature mechanical resistance, Clearflex FG 336 is suggested for the production of freezer bags, either in coextrusion and in blend with LDPE.
| Главная Информация | |
|---|
| Добавка | - Антиблок
- Антиоксидант
- Обработка помощи
- Комбинация
|
| Характеристики | - Антиблокировка
- Антиоксидант
- Сополимер
- Приемлемый пищевой контакт
- Хорошая ударопрочность
- Хорошая технологичность
- Хорошая прочность на разрыв
- Хорошая прочность
- Гексен-комномер
- Высокая жесткость
- Низкая плотность
- Комбинация
|
| Используется | |
| Рейтинг агентства | - ЕС пищевой контакт, неуказанный рейтинг
|
| Формы | |
| Метод обработки | - Выдувная пленка
- Коэкструзия
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.926 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | 0.11 | | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Толщина пленки-рекомендовано/доступно | 10 to 50µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 1% Secant, MD
: 25 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD
: 25 µm, Blown Film | 200 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 25 µm, Blown Film | 12.0 | MPa | |
| TD
: Yield, 25 µm, Blown Film | 13.0 | MPa | |
| MD
: Break, 25 µm, Blown Film | 45.0 | MPa | |
| TD
: Break, 25 µm, Blown Film | 36.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 25 µm, Blown Film | 550 | % | |
| TD
: Break, 25 µm, Blown Film | 740 | % | |
| Ударное падение Dart 1(25 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | | | ISO 6383-2 |
| MD
: 25.0 µm | 82.0 | kN/m | |
| TD
: 25.0 µm | 250.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -70.0 | °C | ASTM D746 |
| Викат Температура размягчения | 110 | °C | ISO 306/A |
| Температура плавления | 127 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 25.0 µm, Blown Film) | 54 | | ASTM D2457 |
| Haze (25.0 µm, Blown Film) | 13 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 190 to 230 | °C | |
| Примечание |
|---|
| 1 . | F50 |
| 2 . | Blown Film |