Braskem PE STS7006
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Braskem America Inc. |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
mYH9q9_Braskem-PE-STS7006.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Description: STS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides STS7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. The minimum biobased content of this grade is 95%, determined according to ASTM D6866.
Additives: Antiblocking. Slip agent.
Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc.
Process: Blown Film Extrusion.
Additives: Antiblocking. Slip agent.
Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc.
Process: Blown Film Extrusion.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.924 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 140 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 170 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 700 | % | ASTM D882 |
| Ударное падение Dart 1(50 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 310 | g | ASTM D1922 |
| TD : 50 µm, blown film | 250 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск | ASTM D2457 | ||
| 45, blown film | 60 | ASTM D2457 | |
| 60, blown film | 84 | ASTM D2457 | |
| Haze (Blown Film) | 9.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Двуслойное содержание | > 95 | % | ASTM D6866 |
| Blown Film Properties: 50µm thickness film, processed in a 50mm blow film line with barrier screw. 25:1 L/D and a 1.0 mm die gap at a 2.3: 1 blow up ratio.Recommended processing conditions:Blow Film ExtrusionTemperature Profile:……....from 150 to 185°CMass Temperature:........... from 180 to 185°CBlow up Ratio:…………….….from 2,0 to 3,0:1Die Gap:………………………..1,0 mm |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| RELENE® 1020FA20 | LDPE | Reliance Industries Limited |
| Yanshan PE LD100BW | LDPE | SINOPEC Beijing Yanshan Petrochemical |
| DOW™ LDPE 206M | LDPE | The Dow Chemical Company |
| Aaron AVPE LD 300-1 | LDPE | Aaron Industries Corp. |
| Hanwha Total PE 531G | LDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Petrothene® M2520FN | LDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved