Описание материалов:
MMF-1237 is a certified prime grade Hexene copolymer HIGH MOLECULAR WEIGHT developed for production of industrial films of outstanding Stress Cracking Resistance. MMF-1237 features BROAD molecular weight distribution, easy processability, excellent melt strength, broad fusion sealing range, good balance of film mechanical properties, and meets the requirements of GR -GM13. MMF-1237 applications include Pond liners, Gas and Chemical containment liners, Landfill liners, and Geomembranes. Other suggested blown film applications include shopping bags, small shoppers, lamination films, wrapping films, multi-wall bag liners, and tablecloths. Minimum recommended film gauge is 12 microns (0.5 mil), and processing temperature 195° to 300°C. MMF-1237 complies with FDA regulation 21CFR 177.1520 (c) 3.2(a) and most international regulations concerning the use of Polyethylene in contact with food.
| Главная Информация | |
|---|
| Характеристики | - Широкий диапазон уплотнения
- Высокий уровень ЭСКП (устойчивость к растрескиванию)
- Высокая Молекулярная масса
- Сополимер
- Гексен-комномер
- Обрабатываемость, хорошая
- Широкое молекулярное распределение веса
- Хорошая прочность расплава
- Соответствие пищевого контакта
|
| Используется | - Гео мембраны
- Пленка
- Ламинат
- Подкладка
- Сумка
- Промышленное применение
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.2a
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.937 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/2.16 kg | 0.12 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 12 | g/10 min | ASTM D1238 |
| Экологическое сопротивление растрескиванию 1 | | | |
| 50°C, 1.75mm, 10% Igepal, molded, F50 | > 1500 | hr | ASTM D1693B |
| 100°C, 1.75mm, 100% Igepal, molded, F50 | > 1500 | hr | ASTM D1693C |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Yield, Compression Molded) | 18.5 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, Compression Molded) | > 700 | % | ASTM D638 |
| Флекторный модуль (Compression Molded) | 800 | MPa | ASTM D790 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки-рекомендовано/доступно | Minimum 12 µm (0.5 mil) | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Пиковая температура плавления | 126 | °C | ASTM D3417 |
| Дополнительная информация |
|---|
| Test specimens from compression molded plaque according to ASTM D 1928 Procedure C. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 195 - 300 | °C | |
| Примечание |
|---|
| 1 . | Notched bent strip |