Riblene® FC 39 D
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Versalis S.p.A. |
| Торговая марка | Riblene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
imFfPM_Riblene-FC-39-D.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Riblene FC 39 D is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion.
Riblene FC 39 D is characterised by a high melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene FC 39 D are easily heat shrinkable and characterised by high rigidity, good mechanical and optical properties.
Main Application
Riblene FC 39 D is recommended for the production of medium rigidity shrink film characterized by good clarity and gloss.
Riblene FC 39 D is characterised by a high melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene FC 39 D are easily heat shrinkable and characterised by high rigidity, good mechanical and optical properties.
Main Application
Riblene FC 39 D is recommended for the production of medium rigidity shrink film characterized by good clarity and gloss.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.924 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 70 | µm | |
| Толщина пленки-рекомендовано/доступно | 40 to 150 µm | ||
| Модуль растяжения | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 28.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 26.0 | MPa | |
| Удлинение при растяжении | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 450 | % | |
| TD : Break, 70 µm, Blown Film | 600 | % | |
| Ударное падение Dart 1(70 µm, Blown Film) | 310 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 30.0 | kN/m | |
| TD : 70.0 µm | 45.0 | kN/m |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура ломкости | < -75.0 | °C | ASTM D746 |
| Викат Температура размягчения | 93.0 | °C | ISO 306/A |
| Температура плавления | 114 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 70.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 8.0 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 180 to 220 | °C |
| Примечание | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Тип материала | Категория | Производитель |
|---|---|---|
| SABIC® LDPE 2102X0 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| Sasol Polymers PE LT159 (Extrusion/Blow molding) | LDPE | Sasol Polymers |
| Westlake LDPE EC476AA | LDPE | Westlake Chemical Corporation |
| NEXUS PE LDPE-818 | LDPE | Nexus Resin Group, LLC. |
| Bynel® 4206 | LDPE | DuPont Packaging & Industrial Polymers |
| HANWHA CLNA-8141EHV | LDPE | Hanwha Chemical |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved