Описание материалов:
LL6608AF has been developed for lean and rich blend blown film applications, such as rigid layers in coextrusion, carrier bags, refuse sacks and liners. This grade is also recommended for artificial grass applications.
LL6608AF is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.
We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL6608AF.
LL6608AF is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
- Optimum balance between stiffness and film strength
- Good optical properties
- Good bubble stability
- Excellent sealability and hot-tack strength
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.
We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL6608AF.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Соответствие RoHS |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.928 | g/cm³ | ISO 1183/D |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 38 | µm | |
| Модуль растяжения- 1% Secant (38 µm, Blown Film) | 290 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, blown film | 14.0 | MPa | ISO 527-3 |
| TD : Yield, 38 µm, blown film | 16.0 | MPa | ISO 527-3 |
| MD : 38 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : 38 µm, blown film | 35.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | ISO 527-3 | ||
| MD : Broken, 38 µm, blown film | 750 | % | ISO 527-3 |
| TD : Broken, 38 µm, blown film | 900 | % | ISO 527-3 |
| Ударное падение Dart (38 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38.0 µm | 43.1 | kN/m | ASTM D1922 |
| TD : 38.0 µm | 255.0 | kN/m | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 116 | °C | ISO 306/A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 38.0 µm, Blown Film) | 56 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 190 - 230 | °C |
| Примечание | |
|---|---|
| 1 . | Blown Film |
| Тип материала | Категория | Производитель |
|---|---|---|
| Premier LB01018 - D | LLDPE | Premier Polymers, LLC. |
| SureSpec LLC4-200 | LLDPE | Genesis Polymers |
| TITANCEED® mL156 | LLDPE | Lotte Chemical Titan (M) Sdn. Bhd. |
| ETILINAS LL0220AA | LLDPE | POLYETHYLENE MALAYSIA SDN BHD |
| EVALENE® LLDPE LJ20241 | LLDPE | JG Summit Petrochemical Corporation |
| Osterlene® LL01020SA | LLDPE | Osterman & Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved