Описание материалов:
Andur M-33 is a low melting MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in low temperature applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 96 | | ASTM D2240 |
| Shaw D | 42 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 0.621 | MPa | ASTM D695 |
| 5% strain | 2.69 | MPa | ASTM D695 |
| 10% strain | 4.14 | MPa | ASTM D695 |
| 15% strain | 5.45 | MPa | ASTM D695 |
| 20% strain | 6.76 | MPa | ASTM D695 |
| 25% strain | 8.20 | MPa | ASTM D695 |
| 50% strain | 26.7 | MPa | ASTM D695 |
| Устойчивость к истиранию | 29.0 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 12.2 | MPa | ASTM D412 |
| 300% strain | 14.8 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 18.4 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 510 | % | ASTM D412 |
| Комплект сжатия | 21 | % | ASTM D395 |
| Сопротивляемость Bayshore | 45 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 6.0 - 8.0 | min | |
| Время демолд | 45 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 695 pliAverage Split Tear, ASTM D1938: 170 pliStoichiometry Curative Level: 97%NBS Abrasion: 240% Rubber StandardParts of curative per 100 parts Andur M-33, 6.75% NCO: 15.15 parts by weightParts of curative per 100 parts Andur M-33, 6.8% NCO: 15.26 parts by weightParts of curative per 100 parts Andur M-33, 6.85% NCO: 15.38 parts by weightParts of curative per 100 parts Andur M-33, 6.9% NCO: 15.49 parts by weightParts of curative per 100 parts Andur M-33, 6.95% NCO: 15.6 parts by weightParts of curative per 100 parts Andur M-33, 7% NCO: 15.71 parts by weightMix Temperature:
Andur M-33: 212°F
Curative HQEE: 77-158°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 110 - 140 | °C | |
| Тип материала |
Категория |
Производитель |
|
Xuchuan XCNS 3001 C-B |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Andur 1-83 AP |
PUR-Ether/TDI |
Anderson Development Company
|
|
Xuchuan XCW-6400M |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
ChronoFlex® C 80A |
PUR, Unspecified |
CardioTech International, Inc.
|
|
Evermore PUR SS-1058NHR |
PUR, Unspecified |
Evermore Chemical Industry Co., Ltd.
|
|
Huafon JF-S-AH8100 |
PUR, Unspecified |
Huafon Group Co., Ltd.
|