Описание материалов:
Lustran ABS 1152 resin is a very high-impact extrusion grade of ABS (acrylonitrile butadiene styrene) with a balance of properties not offered by other grades of ABS. It offers superior toughness, particularly for low-temperature applications, and good thermoformability. It is easy to color with ABS color concentrates.
Lustran ABS 1152 resin is used in extrusion applications where super toughness is a prime consideration. Typical applications include vehicle instrument panels, luggage shells, agricultural equipment, and construction equipment. It is also used as a substrate under other specialty grade, such as Lustran ABS 556 low gloss resin and Centrex® weatherable polymers. As with any product, use of Lustran ABS 1152 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Прочность при низкой температуре
- Высокая ударопрочность
- Хорошая прочность
|
| Используется | - Область архитектурного применения
- Сельскохозяйственное применение
- Кожаный чехол
- Приборная панель автомобиля
|
| Рейтинг агентства | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.03 | g/cm³ | ASTM D792 |
| Удельный объем | 0.970 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/10.0 kg) | 7.3 | g/10 min | ASTM D1238 |
| Поглощение воды 1(23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 93 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ASTM D638 |
| -18°C | 2210 | MPa | ASTM D638 |
| 23°C | 1520 | MPa | ASTM D638 |
| 71°C | 1240 | MPa | ASTM D638 |
| Прочность на растяжение | | | ASTM D638 |
| Yield, -18°C | 40.7 | MPa | ASTM D638 |
| Yield, 23°C | 31.0 | MPa | ASTM D638 |
| Yield, 71°C | 19.3 | MPa | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| -40°C | 2000 | MPa | ASTM D790 |
| 23°C | 1790 | MPa | ASTM D790 |
| 71°C | 1380 | MPa | ASTM D790 |
| Flexural Strength | | | ASTM D790 |
| Yield, -40°C | 80.7 | MPa | ASTM D790 |
| Yield, 23°C | 48.3 | MPa | ASTM D790 |
| Yield, 71°C | 32.4 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C, 3.18 mm | 220 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 350 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| Ударное устройство для дротиков 2 | | | ASTM D3763 |
| -40°C, Peak Energy 3 | 31.2 | J | ASTM D3763 |
| -40°C, Total Energy 4 | 35.3 | J | ASTM D3763 |
| -18°C, Peak Energy 5 | 33.9 | J | ASTM D3763 |
| -18°C, Total Energy 6 | 47.5 | J | ASTM D3763 |
| 23°C, Peak Energy 7 | 29.8 | J | ASTM D3763 |
| 23°C, Total Energy 8 | 50.2 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 89.4 | °C | ASTM D648 |
| 0.45 MPa, annealed | 96.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, annealed | 90.6 | °C | ASTM D648 |
| CLTE-
Поток | 1.0E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 60.0 | °C | UL 746 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость горения 9(3.18 mm) | 36 | mm/min | ASTM D635 |
| Огнестойкость (1.50 mm) | HB | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60 °, extruded sheet) | 80 | | ASTM D523 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 - 93.3 | °C | |
| Время сушки | 3.0 - 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.030 | % | |
| Зона цилиндра 1 темп. | 216 - 241 | °C | |
| Зона цилиндра 2 температура. | 216 - 241 | °C | |
| Зона цилиндра 3 темп. | 216 - 241 | °C | |
| Зона цилиндра 4 темп. | 216 - 241 | °C | |
| Зона цилиндра 5 темп. | 216 - 241 | °C | |
| Температура расплава | 216 - 249 | °C | |
| Температура матрицы | 210 - 241 | °C | |
| Рулон для снятия | 62.8 - 104 | °C | |
| Инструкции по экструзии |
|---|
| Max Regrind Allowed: 40% |
| Примечание |
|---|
| 1 . | Injection Molded specimen |
| 2 . | 0.5 in dart, 3 in clamp |
| 3 . | 3.40 m/sec |
| 4 . | 3.40 m/sec |
| 5 . | 2.32 m/sec |
| 6 . | 3.40 m/sec |
| 7 . | 3.40 m/sec |
| 8 . | 3.40 m/sec |
| 9 . | Injection Molded specimen |