Andur 700-APX/Curene® 442
Описание материалов:
Andur® 700-APX represents Anderson Development Company's continued effort to provide high performance, moderate cost, prepolymers for the cast urethane industry. It is a polyester/ether based, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 70 Shore A is obtained when this prepolymer is cured with Curene® 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur® 700-APX with polyols and their combination with Curene® 442 and other diamines or through the use of plasticizers.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | |
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 70 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 17.0 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 890 | % | ASTM D638 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 2.28 | MPa | ASTM D412 |
| 300% strain | 3.24 | MPa | ASTM D412 |
| Комплект сжатия | 42 | % | ASTM D395B |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Срок службы горшка | 10 - 12 | min | |
| Терморегулирующая вязкость (70°C) | 1000 | cP | ASTM D2393 |
| Время демолд | 45 | min | |
| Время доставки (93°C) | 16 | hr | |
| Дополнительная информация |
|---|
| All properties based on Andur® 700-APX cured with Curene® 442.The value listed as Split Tear, ASTM D470 was tested in accordance with ASTM D1938.The value listed as Elongation@Break, ASTM D638 was tested in accordance with ASTM D412.%NCO: 3.0-3.4Viscosity, cps@70°F: waxViscosity, cps@212°F: 300Specific Gravity@212°F: 1.08Rebound, ASTM D2632 %: 46Curene® 442 Level, % Stoichiometry: 95%Andur® 700-APX Mix Temperature, °F: 180-212Curene® 442 Mix Temperature, °F: 230-250Split Tear, ASTM D470: 81 pliCompression/Deflection, ASTM D575, psi5%: 5910%: 12315%: 20525%: 311Recommended Cure Time @ 150-160°F: Overnight |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 104 - 113 | °C | |