TOTAL Polyethylene HDPE D4720
| Категория | HDPE, High Density (MMW) Polyethylene , HDPE, MMW |
| Производитель | TOTAL Refining & Chemicals |
| Торговая марка | TOTAL Polyethylene |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
baaxRS_TOTAL-Polyethylene-HDPE-D4720.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
HDPE 4720 Polyethylene:
Medium Molecular Weight High Density Film Resin
Characteristics
Applications
Medium Molecular Weight High Density Film Resin
Characteristics
- Excellent processability
- Good tear and impact strength
- Good stiffness
- Excellent compatibility with LDPE and LLDPE
- Excellent drawdown
- Good moisture barrier properties
Applications
- Multi-wall liner
- Gas flush poultry bags
- Mailing envelopes
- Heavy-duty shipping sacks
- Fresh cut produce packaging
- Coextrusions
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.947 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.28 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль 1 | ASTM D882A | ||
| 1% Secant, MD : 25 µm | 710 | MPa | |
| 1% Secant, TD : 25 µm | 1000 | MPa | |
| Прочность на растяжение | ASTM D882A | ||
| MD : Yield, 25 µm 2 | 24.1 | MPa | |
| MD : Yield, 25 µm 3 | 23.4 | MPa | |
| TD : Yield, 25 µm 4 | 25.5 | MPa | |
| TD : Yield, 25 µm 5 | 26.2 | MPa | |
| MD : Break, 25 µm 6 | 4.83 | MPa | |
| MD : Break, 25 µm 7 | 62.1 | MPa | |
| TD : Break, 25 µm 8 | 39.3 | MPa | |
| TD : Break, 25 µm 9 | 18.6 | MPa | |
| Удлинение при растяжении | ASTM D882A | ||
| MD : Break, 25 µm 10 | 600 | % | |
| MD : Break, 25 µm 11 | 450 | % | |
| TD : Break, 25 µm 12 | 700 | % | |
| TD : Break, 25 µm 13 | 600 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm 14 | 28 | g | |
| MD : 25 µm 15 | 10 | g | |
| TD : 25 µm 16 | 530 | g | |
| TD : 25 µm 17 | 1500 | g | |
| Скорость передачи водяного пара 18(38°C, 25 µm) | 7.8 | g/m²/24 hr | ASTM E96 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления | 131 | °C | ASTM D3417 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Dart Impact | ASTM D1709 | ||
| 25.4 µm 19 | 100 | g | |
| 25.4 µm 20 | < 50 | g |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 193 to 216 | °C |
| Примечание | |
|---|---|
| 1 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 2 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 3 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 4 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 5 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 6 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 7 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 8 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 9 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 10 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 11 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 12 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 13 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 14 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 15 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 16 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 17 . | Film was produced at 1.0 mil with a 2.5 BUR |
| 18 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 19 . | High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR |
| 20 . | Film was produced at 1.0 mil with a 2.5 BUR |
| Тип материала | Категория | Производитель |
|---|---|---|
| PRIMATOP HDPE 080960 | HDPE | Amco Polymers |
| DOW™ HDPE DMDC-7950 NT 7 | HDPE | The Dow Chemical Company |
| NPC PE HD-5502GA | HDPE | NPC Alliance Corporation |
| HIVOREX 2600J | HDPE | Lotte Chemical Corporation |
| Hostalen ACP 7740 F3 | HDPE | LyondellBasell Industries |
| Braskem PE HDP3049 | HDPE | Braskem IDESA |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved