Capran® 1200 Matte

Категория	PA6, Polyamide 6 , Nylon 6
Производитель	Honeywell
Торговая марка	Capran®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	asv1Ow_Capran-1200-Matte.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

CAPRAN® 1200 Matte is a nominal 0.55 mil (14 micron) biaxially oriented nylon 6 film with a matte appearance on one side. The matte surface imparts excellent contact clarity while maintaining superior scuff resistance. The combination of properties makes this film well suited for use in thermal lamination films designed for book cover applications.

Главная Информация
Характеристики	Устойчивость к царапинам Высокое разрешение
Используется	Двухосно-ориентированная пленка Защитный чехол
Внешний вид	Шероховатая отделка
Формы	Пленка

Механические	Номинальное значение	Метод испытания
Коэффициент трения		ASTM D1894
With Metal-Dynamic	0.45	ASTM D1894
With self-dynamics	0.65	ASTM D1894

Пленки	Номинальное значение	Единица измерения	Метод испытания
Толщина пленки протестирована	14	µm
Сектантный модуль			ASTM D882
MD : 14 µm	3100	MPa	ASTM D882
TD : 14 µm	3100	MPa	ASTM D882
Прочность на растяжение			ASTM D882
MD : Broken, 14 µm	234	MPa	ASTM D882
TD : Broken, 14 µm	234	MPa	ASTM D882
Удлинение при растяжении			ASTM D882
MD : Broken, 14 µm	83	%	ASTM D882
TD : Fracture	83	%	ASTM D882

Оптический	Номинальное значение		Метод испытания
Блеск (60°, 14.0 µm)	7 - 9		ASTM D2457

Дополнительная информация
Yield: 43300 in²/lbTensile Strength @ Break, ASTM D 882, MD: 28000 to 40000 psiTensile Strength @ Break, ASTM D 882, TD: 28000 to 40000 psiElongation @ Break, ASTM 882, MD: 65 to 100%Elongation @ Break, ASTM 882, TD: 65 to 100%Secant Modulus, ASTM D 882, MD: 375000 to 500000 psiSecant Modulus, ASTM D 882, TD: 375000 to 500000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1300 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1300 g/milCoefficient of Friction, ASTM D 1894: 0.50 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.40 to 0.50 vs Metal-DynamicSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.0 to 2.0% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0 to 0.5% shrinkagePuncture Strength, ASTM D1306: 925 g

Дополнительная информация

Yield: 43300 in²/lbTensile Strength @ Break, ASTM D 882, MD: 28000 to 40000 psiTensile Strength @ Break, ASTM D 882, TD: 28000 to 40000 psiElongation @ Break, ASTM 882, MD: 65 to 100%Elongation @ Break, ASTM 882, TD: 65 to 100%Secant Modulus, ASTM D 882, MD: 375000 to 500000 psiSecant Modulus, ASTM D 882, TD: 375000 to 500000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1300 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1300 g/milCoefficient of Friction, ASTM D 1894: 0.50 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.40 to 0.50 vs Metal-DynamicSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.0 to 2.0% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0 to 0.5% shrinkagePuncture Strength, ASTM D1306: 925 g

Тип материала	Категория	Производитель
WELLAMID Nylon 6000/52 GV 15 HWUVCP	Nylon 6	CP-Polymer-Technik GmbH & Co. KG
Akulon® K240-HPG3	Nylon 6	DSM Engineering Plastics
CP PRYME® Nylon 6 N100HSL	Nylon 6	Chase Plastics Services Inc.
Clariant Nylon 6 PA-211CF30	Nylon 6	Clariant Corporation
LUVOCOM® 3-8920/BL/L	Nylon 6	Lehmann & Voss & Co.
Tarnamid® T-27 GF25 MT15	Nylon 6	Grupa Azoty S.A.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

