Описание материалов:
Indothene-HD 45GP004 is a natural coloured PE 80 (MRS 8 MPa*) material for pipe extrusion, produced by Stirred Tank Heavy Diluent (STHD) Slurry process. It possesses bimodal molecular weight distribution, which improves processability.
This grade meets the MFI, Density & Hydrostatic strength requirements of material grade PE 80 as per IS:4984:1995 on "High Density Polyethylene pipe for water supply-specification". The designation of the natural resin of 45GP004 is PE-ENA-C45-T006 as per IS:7328-1992 and shall meet the same given in the amendment No. 2 of IS:4984:1995. When incorporated with adequate quantity of carbon black as specified in clause 5.2.3 of IS:4984:1995, will meet the requirements of the designation PE-EW-C45-T006 mentioned in the clause 5.2 of IS:4984:1995.
This grade meets the requirements of Indian Standard IS-10146-1982 on "Polyethylene for its safe use in contact with food stuffs, pharmaceuticals and drinking water". It also conforms to the positive list of constituents as approved in IS:10141:1982. The grade complies with FDA regulation : CFR title 21 , 177.1520, Olefin polymer. The level of antioxidant in 45GP004 is not more than 0.3% by mass of the resin.
| Главная Информация | |
|---|
| Характеристики | - Соответствие пищевого контакта
|
| Используется | |
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
- PPI PE-80
|
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзионная формовка труб
- Экструзия
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.945 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/21.6 kg | 12 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.45 | g/10 min | ASTM D1238 |
| Экологическое сопротивление растрескиванию (Injection Molded, F50) | > 1000 | hr | ASTM D1693 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение 1(Yield, 3.20 mm, Injection Molded) | 27.0 | MPa | ASTM D638 |
| Удлинение при растяжении 2(Break, Compression Molded) | 600 | % | ASTM D638 |
| Флекторный модуль 3(3.20 mm, Injection Molded) | 800 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (3.20 mm, Injection Molded) | No Break | | ASTM D256 |
| Дополнительная информация |
|---|
| Hydrostatic Pressure Test, ISO 1167, 9 MPa, 20°C: >100 hrsHydrostatic Pressure Test, ISO 1167, 4.6 MPa, 80°C: >165 hrsHydrostatic Pressure Test, ISO 1167, 4 MPa, 80°C: >1000 hrsMRS, ISO TR9080: >8.0 MPaSCG, ISO 13479: >165 hrsRCP, ISO 13477: >12 barTensile Elongation at Break, ASTM D 638, Type IV, 3.2 mm: >600% |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 190 | °C | |
| Зона цилиндра 2 температура. | 210 | °C | |
| Зона цилиндра 3 темп. | 220 | °C | |
| Зона цилиндра 4 темп. | 230 | °C | |
| Температура матрицы | 225 | °C | |
| Примечание |
|---|
| 1 . | Type 1 |
| 2 . | Type 4 |
| 3 . | Type 1 |