Edgetek™ ET6000-5009 NHFR White VN-3902
Описание материалов:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность 1(23°C) | 1.19 | g/cm³ | ISO 1183 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C, 4.00 mm, Injection Molded) | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm) | 75.0 | MPa | ISO 527-2/5 |
| Растяжимое напряжение (Break, 23°C, 4.00 mm, Injection Molded) | 3.3 | % | ISO 527-2/5 |
| Флекторный модуль | 3200 | MPa | ISO 178 |
| Флекторный стресс | 110 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (23°C, Injection Molded) | > 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 55 | kJ/m² | ISO 179 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.2 mm) | V-0 | | UL 94 |
| Индекс воспламеняемости провода свечения (3.2 mm) | 960 | °C | IEC 60695-2-12 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 80 | °C | |
| Время сушки | 4.0 | hr | |
| Температура обработки (расплава) | 250 - 280 | °C | |