Описание материалов:

Chemlon® E-66 GF15 is an economy range 15% glass fibre reinforced Nylon 66 compound.
It is available in natural or black versions.

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал, 15% наполнитель по весу
Внешний вид	Черный Натуральный цвет
Метод обработки	Литье под давлением

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.25	g/cm³	ISO 1183
Формовочная усадка ¹	0.30 - 0.80	%	Internal method
Поглощение воды (Equilibrium, 23°C, 50% RH)	2.2	%	ISO 62

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	5200	MPa	ISO 527-2
Tensile Stress (Break)	110	MPa	ISO 527-2
Растяжимое напряжение (Break)	4.0	%	ISO 527-2
Флекторный модуль	4700	MPa	ISO 178
Флекторный стресс ²	140	MPa	ISO 178

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Зубчатый изод Impact	7.0	kJ/m²	ISO 180

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature
0.45 MPa, not annealed	> 230	°C	ISO 75-2/B
1.8 MPa, not annealed	210	°C	ISO 75-2/A

Инъекция	Номинальное значение	Единица измерения
Температура сушки	80.0	°C
Время сушки	2.0	hr
Задняя температура	275 - 300	°C
Средняя температура	275 - 300	°C
Передняя температура	275 - 300	°C
Температура обработки (расплава)	< 300	°C
Температура формы	80.0 - 90.0	°C
Скорость впрыска	Fast
Screw Speed	50 - 200	rpm

Инструкции по впрыску
Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.

Инструкции по впрыску

Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.

Примечание
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At Break

Примечание

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At Break

Тип материала	Категория	Производитель
RTP 200H TFE 10 SI 2	Nylon 66	RTP Company
SLOVAMID® 66 SHI	Nylon 66	Plastcom
Ultramid® Endure D3G10 BK20560	Nylon 66	BASF Corporation
LNP™ LUBRILOY™ RF203AXH compound	Nylon 66	SABIC Innovative Plastics
OnForce™ LFT LF6600-5013 Grey	Nylon 66	PolyOne Corporation
SCHULAMID® 66 MK 30 HI H K1357 GRAU 967370	Nylon 66	A. Schulman Europe

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

