Описание материалов:
Andur 6-DP-LM is a polyester based, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 60 Shore D is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 61 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 5% strain | 1.91 | MPa | ASTM D695 |
| 10% strain | 7.82 | MPa | ASTM D695 |
| 15% strain | 12.6 | MPa | ASTM D695 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 19.7 | MPa | ASTM D412 |
| 300% strain | 38.4 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 56.7 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 400 | % | ASTM D412 |
| Комплект сжатия | 35 | % | ASTM D395B |
| Сопротивляемость Bayshore | 44 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 3.0 | min | |
| Время демолд | 30 | min | |
| Время доставки (96°C) | 16 | hr | |
| Дополнительная информация |
|---|
| Durometer Hardness, ASTM D2240, Shore D: 58 to 63Die C Tear, ASTM D1004: 705 pliAverage Split Tear, ASTM D1938: 422 pliStoichiometry Curative Level: 95%Mix Temperature:
Andur 6 DPLM: 158-180°F
Curene 442: 230-250°F |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 104 - 113 | °C | |