SABIC® SUPEER™ 8318
| Категория | mLLDPE, Metallocene Linear Low Density Polyethylene |
| Производитель | Saudi Basic Industries Corporation (SABIC) |
| Торговая марка | SABIC® SUPEER™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
BXGqYq_SABICSUPEER8318.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
SABIC® SUPEER™ 8318 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of high performance LLDPE cast film applications and has good impact strength and transparency.
SABIC® SUPEER™ 8318 does not contain slip and anti-block agent.
Application
Typical applications for SABIC® SUPEER™ 8318 are stretch wrap film, silage film and breathable film.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
SABIC® SUPEER™ 8318 does not contain slip and anti-block agent.
Application
Typical applications for SABIC® SUPEER™ 8318 are stretch wrap film, silage film and breathable film.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.918 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 40 | µm | |
| Прочность на растяжение | ASTM D882 | ||
| MD : yield, 40 µm, extruded film | 9.80 | MPa | ASTM D882 |
| TD : yield, 40 µm, extruded film | 9.50 | MPa | ASTM D882 |
| MD : broken, 40 µm, extruded film | 49.0 | MPa | ASTM D882 |
| TD : broken, 40 µm, extruded film | 54.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : broken, 40 µm, extruded film | 600 | % | ASTM D882 |
| TD : broken, 40 µm, extruded film | 650 | % | ASTM D882 |
| Ударное падение Dart 1(40 µm, cast film) | 400 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, cast film | 10 | g | ASTM D1922 |
| TD : 40 µm, cast film | 23 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления | 115 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Haze (40.0 µm, cast film) | 2.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура плавления литой пленки | 250 - 300 | °C | |
| Properties have been measured on cast film of 40µm |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| PRIMALENE WPP692M | mLLDPE | Southern Polymer, Inc. |
| ICORENE® 3901 | mLLDPE | ICO Polymers APAC, A Division of A. Schulman |
| MARPOL® LL6R 804UV | mLLDPE | Marco Polo International, Inc. |
| Starflex GM1510BA | mLLDPE | LyondellBasell Industries |
| Daelim Po1y® XP9100 | mLLDPE | DAELIM INDUSTRIAL CO., LTD. |
| Daelim Po1y® XP9400 | mLLDPE | DAELIM INDUSTRIAL CO., LTD. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved