TOTAL Polyethylene HDPE 1285
| Категория | HDPE, High Density (HMW) Polyethylene , HDPE, HMW |
| Производитель | TOTAL Refining & Chemicals |
| Торговая марка | TOTAL Polyethylene |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
AxMEKu_TOTAL-Polyethylene-HDPE-1285.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
TOTAL Polyethylene 1285 is a high density polyethylene material,. This product is available in North America and is processed by co-extrusion molding.
The main features of TOTAL Polyethylene 1285 are:
Typical application areas include:
The main features of TOTAL Polyethylene 1285 are:
- Comply with REACH standard
- high molecular weight
- Good processability
- Good tear strength
- Impact resistance
Typical application areas include:
- bag/lining
- Movie
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.950 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 9.0 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.31 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 20 | µm | |
| Сектантный модуль 1 | ASTM D882A | ||
| 2% secant, MD : 20 µm | 841 | MPa | ASTM D882A |
| 2% secant, TD : 20 µm | 910 | MPa | ASTM D882A |
| Прочность на растяжение 2 | ASTM D882A | ||
| MD : Yield, 20 µm | 36.5 | MPa | ASTM D882A |
| TD : Yield, 20 µm | 34.5 | MPa | ASTM D882A |
| MD : Break, 20 µm | 61.4 | MPa | ASTM D882A |
| TD : Break, 20 µm | 58.6 | MPa | ASTM D882A |
| Удлинение при растяжении 3 | ASTM D882A | ||
| MD : Break, 20 µm | 300 - 500 | % | ASTM D882A |
| TD : Break, 20 µm | 300 - 500 | % | ASTM D882A |
| Ударное падение Dart (20 µm) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 24 | g | ASTM D1922 |
| TD : 20 µm | 120 | g | ASTM D1922 |
| Скорость передачи водяного пара (38°C, 20 µm) | 12 | g/m²/24 hr | ASTM F1249 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления | 127 | °C | DSC |
| Дополнительная информация |
|---|
| Film properties produced on 50 mm Alpine extruder with a 4:1 BUR, at 0.8 mil. |
| Примечание | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Тип материала | Категория | Производитель |
|---|---|---|
| Arak HDPE EX2 | HDPE | Shazand (Arak) Petrochemical Corporation |
| Chemical Resources HD07960 | HDPE | Chemical Resources, Inc. |
| HIVOREX 2210JU | HDPE | Lotte Chemical Corporation |
| Hostalen CRP 100 black (XL) | HDPE | LyondellBasell Industries |
| ICORENE® 1050 | HDPE | ICO Polymers EMEA, A Division of A. Schulman |
| Osterlene® HB3553Z | HDPE | Osterman & Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved