Teflon® PFA TE9725
| Категория | PFA, Perfluoroalkoxy |
| Производитель | DuPont Fluoropolymers |
| Торговая марка | Teflon® PFA |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
6IvrC0_Teflon-PFA-TE9725.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
For inventory control purposes product name may be followed by an X.
Products labeled PFA TE9725 and PFA TE9725 X are equivalent and all information in this document is applicable to both.
Typical Application
DuPont™ Teflon ® PFA TE9725 is an ideal resin for applications involving compounding and compression molding, as well as extruded tubing and other profiles for hose, electrical insulators, and sleeving; industrial film and products made from film; and injection or blow-molded articles requiring superior electrical, chemical, and thermal properties. Teflon ® PFA TE9725 offers a slightly lower melt flow rate than Teflon ® PFA TE9724, ultimately providing a higher degree of stress-crack resistance.
Description
DuPont™ Teflon ® PFA TE9725 is a general purpose fluoroplastic resin available as loosely compacted fluff. It is intended for use in special application processes in consultation with DuPont. Compared with other grades of Teflon ® PFA, its most unique features are a relatively low flow rate and properties that make it suitable for a variety of processes and demanding end uses, especially compounding and compression molding. Table 1 shows the typical property data for Teflon ® PFA TE9725.
Teflon ® PFA TE9725 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ® PFA TE9725 can be used to improve processing rates. Compared with other thermoplastics, Teflon ® PFA TE9725 provides a superior balance and level of end-use properties at high service temperatures. Teflon ® PFA TE9725 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.
Properly processed products made from neat Teflon ® PFA TE9725 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes and excellent weather resistance.
In a flame situation, products of Teflon ® PFA TE9725 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and dded at a slow rate with very little smoke.
Teflon ® PFA TE9725 meets the requirements of ASTM D3307, Type II
Products labeled PFA TE9725 and PFA TE9725 X are equivalent and all information in this document is applicable to both.
Typical Application
DuPont™ Teflon ® PFA TE9725 is an ideal resin for applications involving compounding and compression molding, as well as extruded tubing and other profiles for hose, electrical insulators, and sleeving; industrial film and products made from film; and injection or blow-molded articles requiring superior electrical, chemical, and thermal properties. Teflon ® PFA TE9725 offers a slightly lower melt flow rate than Teflon ® PFA TE9724, ultimately providing a higher degree of stress-crack resistance.
Description
DuPont™ Teflon ® PFA TE9725 is a general purpose fluoroplastic resin available as loosely compacted fluff. It is intended for use in special application processes in consultation with DuPont. Compared with other grades of Teflon ® PFA, its most unique features are a relatively low flow rate and properties that make it suitable for a variety of processes and demanding end uses, especially compounding and compression molding. Table 1 shows the typical property data for Teflon ® PFA TE9725.
Teflon ® PFA TE9725 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ® PFA TE9725 can be used to improve processing rates. Compared with other thermoplastics, Teflon ® PFA TE9725 provides a superior balance and level of end-use properties at high service temperatures. Teflon ® PFA TE9725 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.
Properly processed products made from neat Teflon ® PFA TE9725 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes and excellent weather resistance.
In a flame situation, products of Teflon ® PFA TE9725 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and dded at a slow rate with very little smoke.
Teflon ® PFA TE9725 meets the requirements of ASTM D3307, Type II
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 2.14 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (372°C/5.0 kg) | 1.7 | g/10 min | ASTM D3307, ISO 12086 |
| Поглощение воды (24 hr) | < 0.030 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Твердость дюрометра (Shore D) | 55 | ASTM D2240, ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность на растяжение (23°C) | 26.0 | MPa | ASTM D3307, ISO 12086 |
| Удлинение при растяжении (Break, 23°C) | 300 | % | ASTM D3307, ISO 12086 |
| Флекторный модуль (23°C) | 625 | MPa | ASTM D790, ISO 178 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления | 305 | °C | ASTM D4591 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сопротивление громкости | 1.0E+18 | ohms·cm | ASTM D257, ISO 1325 |
| Диэлектрическая прочность | |||
| 0.250 mm 1 | 80 | kV/mm | ASTM D149 |
| 0.250 mm | 80 | kV/mm | IEC 60243-1 |
| Диэлектрическая постоянная (1 MHz) | 2.03 | ASTM D150, IEC 60250 | |
| Коэффициент рассеивания (1 MHz) | < 2.0E-4 | ASTM D150, IEC 60250 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Огнестойкость 2 | V-0 | UL 94 | |
| Индекс кислорода | > 95 | % | ASTM D2863, ISO 4589-2 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Мит складной выносливость 3(200.0 µm) | 5.0E+5 | Cycles | ASTM D2176 |
| Weather and Chemical Resistance: Outstanding |
| Примечание | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | These results are based on laboratory tests under controlled conditions and do not reflect performance under actual fire conditions, current rating is a typical theoretical value. |
| 3 . | Depending on fabrication conditions |
| Тип материала | Категория | Производитель |
|---|---|---|
| Fluon® PFA P-65P | PFA | Asahi Glass Co., Ltd. |
| NEOFLON™ AP-211SH | PFA | DAIKIN AMERICA, INC. |
| 3M™ Dyneon™ Fluoroplastic PFA 6525TZ | PFA | 3M Advanced Materials Division |
| 3M™ Dyneon™ Fluoroplastic PFA 6515NZ | PFA | 3M Advanced Materials Division |
| Teflon® PFA TE9725 | PFA | DuPont Fluoropolymers |
| Korton PFA | PFA | Saint Gobain - Norton |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved