Andur 8-6 APSLM/Curene® 3005
Описание материалов:
Andur 8-6APSLM is a polyester based liquid, toluene diisocyanate terminated prepolymer designed to remain liquid at room temperature. Elastomers with a Shore A durometer hardness of 84-87 can be obtained when Andur 8-6APSLM is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be prepared by curing Andur 8-6APSLM with various polyols, combinations of polyols and Curene 442, other diamines, or through the use of plasticizers.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 77 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 3.69 | MPa | ASTM D412 |
| 300% strain | 5.86 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 51.0 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 600 | % | ASTM D412 |
| Комплект сжатия | 25 | % | ASTM D395B |
| Сопротивляемость Bayshore | 34 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 150 | min | |
| Время демолд | 30 | min | |
| Время доставки | | | |
| 22°C | 72 | hr | |
| 99°C | 16 | hr | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 310 pliAverage Split Tear, ASTM D1938: 130 pliStoichiometry Curative Level: 95%Grams Curene 3005 per 100 grams Andur 8 to 6 APSLM: 21.5Mix Temperature:
Andur 8-6 APSLM: 190°F
Curene 3005: 235°F |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 113 | °C | |