Описание материалов:
TECAFORM® is a semi-crystalline thermoplastic offering high strength, stiffness and toughness. TECAFORM® is resistant to hot water, hydrocarbons and solvents, and it possesses good bearing and wear properties. It is available in natural and black grades. TECAFORM® is commonly used as bushings, rollers, wear strips and other applications requiring a combination of strength, low moisture absorption, chemical resistance and dimensional stability.
TECAFORM® is used in a wide variety of industrial applications requiring good strength and toughness, dimensional stability, wear resistance and the ability to operate in a wet environment with little absorption. Material handling, machinery and fluid handling are some of the common industries utilizing TECAFORM®'s combination of properties. Typical applications are gears, wear strips, bushings, pump parts, fittings and rollers.
| Главная Информация | |
|---|
| Характеристики | - Полу-кристаллический
- Хорошая стабильность размеров
- Низкая гигроскопичность
- Жесткий, высокий
- Высокая прочность
- Сополимер
- Основа для защиты от растворителей
- Обрабатываемый
- Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Хорошая стойкость к истиранию
- Устойчивость к углеводородам
- Хорошая прочность
|
| Используется | - Детали Насоса
- Втулка
- Шестерня
- Анти-абразивный полировальный круг палка
- Ролик
- Аксессуары
|
| Рейтинг агентства | |
| Внешний вид | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.41 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 23°C, 24 hr | 0.22 | % | ASTM D570 |
| Saturated, 23°C | 0.80 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (M-Scale) | 86 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2620 | MPa | ASTM D638 |
| Прочность на растяжение (Yield, 23°C) | 60.7 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 23°C) | 25 | % | ASTM D638 |
| Флекторный модуль (23°C) | 2480 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 75.8 | MPa | ASTM D790 |
| Прочность на сжатие | 31.0 | MPa | ASTM D695 |
| Коэффициент трения 1(vs. Itself - Dynamic) | 0.21 | | |
| Коэффициент износа 2(0.28 MPa, 0.25 m/sec) | 130 | 10^-8 mm³/N·m | ASTM D3702 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Незубчатый изод Impact | 53 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| Температура плавления | 165 | °C | ASTM D2133 |
| CLTE-
Поток | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Максимальная температура обслуживания | | | |
| Intermittent | 141 | °C | |
| Long Term 3 | 91 | °C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | 1.0E+14 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность | 20 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная 4(23°C, 60 Hz) | 3.70 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | HB | | UL 94 |
| Дополнительная информация |
|---|
| Data obtained from extruded shapes |
| Примечание |
|---|
| 1 . | 40 psi, 50 fpm |
| 2 . | Against Steel |
| 3 . | UL 746B |
| 4 . | 50% RH |